OEM Customized wholesale Steel Shot-S780 for Ghana Manufacturers
Short Description:
FEAUTRES Size: S780 Diameter: 2.5mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S780 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
OEM Customized wholesale Steel Shot-S780 for Ghana Manufacturers Detail:
FEAUTRES
Size: S780
Diameter: 2.5mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S780
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Basic Information About Abrasive Garnet Processing
Garnet: The Ancient Stone Which Beholds Sheer Class
We insist on offering premium quality manufacturing with superior business concept, honest product sales as well as finest and fast assistance. it will bring you not only the good quality product or service and huge profit, but the most significant is to occupy the endless market for OEM Customized wholesale Steel Shot-S780 for Ghana Manufacturers, The product will supply to all over the world, such as: St. Petersburg, France, Switzerland, Profession, Devoting are always fundamental to our mission. We've got always been in line with serving customers, creating value management objectives and adhering to the sincerity, dedication, persistent management idea.
By Jane from Roman - 2018.06.03 10:17
Cooperate with you every time is very successful, very happy. Hope that we can have more cooperation!
By Steven from Los Angeles - 2017.02.28 14:19