Low price for Steel Shot-S110 to Lisbon Factories
Short Description:
FEATURES Size: S110 Diameter: 0.3mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S110 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Low price for Steel Shot-S110 to Lisbon Factories Detail:
FEATURES
Size: S110
Diameter: 0.3mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S110
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
Basic Information About Abrasive Garnet Processing
We depend on sturdy technical force and continually create sophisticated technologies to meet the demand of Low price for Steel Shot-S110 to Lisbon Factories, The product will supply to all over the world, such as: Oman, Jordan, Belgium, As the world economic integration bringing challenges and opportunities to the xxx industry, our company , by carrying on our teamwork, quality first, innovation and mutual benefit, are confident enough to supply our clients sincerely with qualified merchandise, competitive price and great service, and to build a brighter future under the spirit of higher, faster, stronger with our friends together by carrying on our discipline.
By Griselda from Serbia - 2017.07.28 15:46
Cooperate with you every time is very successful, very happy. Hope that we can have more cooperation!
By Christina from Buenos Aires - 2018.09.29 13:24