factory customized Steel Shot-S70 to Lebanon Factories
Short Description:
FEATURES Size: S70 Diameter: 0.2mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm Grain Distribution of Steel Shot S70 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
factory customized Steel Shot-S70 to Lebanon Factories Detail:
FEATURES
Size: S70
Diameter: 0.2mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm
Grain Distribution of Steel Shot S70
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Benefits of Garnet Abrasives
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
Assume full responsibility to meet all demands of our clients; achieve continuous advancements by promoting the growth of our clients; become the final permanent cooperative partner of clients and maximize the interests of clients for factory customized Steel Shot-S70 to Lebanon Factories, The product will supply to all over the world, such as: Hamburg, Guyana, Tunisia, We expect to provide products and services to more users in global aftermarket markets; we launched our global branding strategy by providing our excellent products all over the world by virtue of our well reputed partners letting global users keep pace with technology innovation and achievements with us.
By Julie from Malaysia - 2018.09.29 17:23
After the signing of the contract, we received satisfactory goods in a short term, this is a commendable manufacturer.
By Christopher Mabey from UAE - 2018.09.12 17:18