Factory Cheap Hot Steel Shot-S550 Wholesale to Nairobi
Short Description:
FEAUTRES Size: S550 Diameter: 1.7mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S550 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Factory Cheap Hot Steel Shot-S550 Wholesale to Nairobi Detail:
FEAUTRES
Size: S550
Diameter: 1.7mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S550
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Basic Information About Abrasive Garnet Processing
Garnet: The Ancient Stone Which Beholds Sheer Class
We have quite a few great team customers very good at internet marketing, QC, and dealing with kinds of troublesome trouble while in the output approach for Factory Cheap Hot Steel Shot-S550 Wholesale to Nairobi, The product will supply to all over the world, such as: Madras, Morocco, Jamaica, Many kinds of different solutions are available for you to choose, you can do one-stop shopping here. And customized orders are acceptable. Real business is to get win-win situation, if possible, we would like to deliver more support for customers. Welcome all nice buyers communicate details of solutions with us!!
By Marguerite from UK - 2017.10.23 10:29
The company can think what our think, the urgency of urgency to act in the interests of our position, can be said this is a responsible company, we had a happy cooperation!
By Erin from Russia - 2017.01.28 19:59