China Manufacturer for Steel Shot-S460 for Buenos Aires Importers
Short Description:
FEAUTRES Size: S460 Diameter: 1.4mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S460 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
China Manufacturer for Steel Shot-S460 for Buenos Aires Importers Detail:
FEAUTRES
Size: S460
Diameter: 1.4mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S460
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Garnet: The Ancient Stone Which Beholds Sheer Class
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
With our leading technology at the same time as our spirit of innovation,mutual cooperation, benefits and advancement, we will build a prosperous future with each other with your esteemed firm for China Manufacturer for Steel Shot-S460 for Buenos Aires Importers, The product will supply to all over the world, such as: Latvia, Dubai, Afghanistan, Certainly, competitive price, suitable package and timely delivery will be assured as per customers' demands. We sincerely hope to build business relationship with you on the basis of mutual benefit and profit in the very near future. Warmly welcome to contact us and become our direct cooperators.
By Merry from Naples - 2018.06.26 19:27
The company has a good reputation in this industry, and finally it tured out that choose them is a good choice.
By Naomi from Netherlands - 2017.02.28 14:19