China Gold Supplier for Steel Shot-S780 for Japan Manufacturers
Short Description:
FEAUTRES Size: S780 Diameter: 2.5mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S780 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
China Gold Supplier for Steel Shot-S780 for Japan Manufacturers Detail:
FEAUTRES
Size: S780
Diameter: 2.5mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S780
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Basic Information About Abrasive Garnet Processing
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
We believe in: Innovation is our soul and spirit. High-quality is our life. Purchaser need is our God for China Gold Supplier for Steel Shot-S780 for Japan Manufacturers, The product will supply to all over the world, such as: Korea, Anguilla, Bangkok, After years' creating and developing, with the advantages of trained qualified talents and rich marketing experience, outstanding achievements were gradually made. We get good reputation from the customers due to our good solutions quality and fine after-sale service. We sincerely wish to create a more prosperous and flourishing future together with all the friends home and abroad!
By Cornelia from Mexico - 2017.03.28 12:22
This is a very professional wholesaler, we always come to their company for procurement, good quality and cheap.
By Maggie from Luxemburg - 2017.09.29 11:19