FEATURES Size: S110 Diameter: 0.3mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S110 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Newly Arrival Steel Shot-S110 to Orlando Manufacturers Detail:
FEATURES
Size: S110
Diameter: 0.3mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S110
TECHNICAL DATA
Name |
Steel Shot |
|
Chemistry |
(C) |
0.70~1.20% |
(Mn) |
0.35~1.20% |
|
(Si) |
0.40~1.20% |
|
(S) |
≤0.05% |
|
(P) |
≤0.05% |
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
Deviation |
±3.0HRC(±40HV) |
|
Micro Structure |
Tempered martensite or tempered troostite |
|
Density |
7.2g/cm3 |
Product detail pictures:
Related Product Guide:
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
Garnet – Stone of Growth, Protection and Healing
We know that we only thrive if we could guarantee our combined price tag competiveness and quality advantageous at the same time for Newly Arrival Steel Shot-S110 to Orlando Manufacturers, The product will supply to all over the world, such as: Zambia , Czech , Cairo , Our advantages are our innovation, flexibility and reliability which have been built during last 20 years. We focus on providing service for our clients as a key element in strengthening our long-term relationships. The continual availability of high grade products in combination with our excellent pre- and after-sales service ensures strong competitiveness in an increasingly globalized market.
By Gabrielle from Moldova - 2018.04.25 16:46
The customer service staff's attitude is very sincere and the reply is timely and very detailed, this is very helpful for our deal,thank you.
By Bernice from San Francisco - 2017.03.08 14:45