FEATURES A kind of artificial abrasive.3 oxidation 2 aluminium (Al2O3) content over 98%, and the composition such as containing a small amount of ferric oxide, silicon oxide, appera white. white aluminium oxide a kind of high grade refractories, was made from the high quality alumina by melting above 2000 in the aluminium oxide grit electric arc furnace and cooling. It is white with the main crystal phase alphaAl2O3. The white alumina produced in titling electric arc furnace has the advantag...
KARATTERISTIĊI
A tip ta 'artifiċjali abrasive.3 kontenut ossidazzjoni 2 aluminju (Al2O3) aktar minn 98%, u l-kompożizzjoni bħal li fihom ammont żgħir ta' ferric oxide, ossidu tas-silikon, appera abjad.
white aluminium oxide a kind of high grade refractories, was made from the high quality alumina by melting above 2000 in the aluminium oxide grit electric arc furnace and cooling. It is white with the main crystal phase alphaAl2O3. The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved.
Daqs naqal: 12 # -220 #
Micropowder: 240#-1200#
karattru
1. Ceramic surface treatment
2. F12-F2000
3. Grinding/Polishing
4. Abjad Aluminju Ossidu
TECHNICAL DATA
użu |
ispeċifikazzjoni |
kimika% |
|||
Al2O3 |
Na2O |
materjal manjetiku% |
SiO2 |
||
barraxi |
F12 # -80 # |
≥99.4 |
≤0.4 |
- |
≤0.03 |
90 # -150 # |
≥99.3 |
≤0.4 |
≤0.03 |
≤0.05 |
|
180 # -240 # |
≥98.2 |
≤0.4 |
- |
≤0.03 |
|
1 # -63 # |
≥99.3 |
≤0.4 |
≤0.03 |
≤0.05 |
|
materjal reżistenti għan-nar |
180 # -0 200 # -0 320 # -0 |
≥99.3 |
≤0.4 |
≤0.06 |
≤0.05 |
trab mikro |
0-1mm 1-3mm 3-5mm 5-8mm 8-12mm |
≥99 |
≤0.4 |
≤0.1 |
≤0.02 |
kompożizzjonijiet kimiċi |
proprjetajiet fiżiċi |
|||
Punti |
Valur ta 'speċifikazzjoni (%) |
Punti |
proprjetà |
|
Al2O3 |
99.18min |
kulur |
abjad |
|
SiO2 |
0.04max |
densità tal-massa |
1.75-1.95g / ċm3 |
|
Na2O |
0.40max |
densità veru |
3.90g / min ċm3 |
|
Fe2O3 |
0.08max |
ebusija |
ebusija Morse |
9 |
ebusija mikro |
21600-22600kg / mm3 |
|||
kontenut tas-sustanza manjetika |
0.0023% mass |
-APPLIKAZZJONI
Barraxi bonded u abbressivi miksija
1.lapping, polishing,decorative non-skid tile, and pressure blasting.
2.Coated Abrasives
3.Surface treatment/finishing
4.Anti-Skid Paints
5.Ceramic Tiles special ceramics
6.Fluidized Bed Furnaces and Skin / Dental Care
7.grinding high carbon steel, high-speed steel and chilled steel