White Aluminium oxide
Mubo nga paghulagway:
FEATURES A kind of artificial abrasive.3 oxidation 2 aluminium (Al2O3) content over 98%, and the composition such as containing a small amount of ferric oxide, silicon oxide, appera white. white aluminium oxide a kind of high grade refractories, was made from the high quality alumina by melting above 2000 in the aluminium oxide grit electric arc furnace and cooling. It is white with the main crystal phase alphaAl2O3. The white alumina produced in titling electric arc furnace has the advantag...
ARTIKULO
Usa ka matang sa artipisyal abrasive.3 oxidation 2 aluminum (Al2O3) sulod sa 98%, ug ang komposisyon sama sa nga naglangkob sa usa ka gamay nga kantidad sa ferric oxide, silicon oxide, appera puti.
white aluminium oxide a kind of high grade refractories, was made from the high quality alumina by melting above 2000 in the aluminium oxide grit electric arc furnace and cooling. It is white with the main crystal phase alphaAl2O3. The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved.
gidak-on grit: 12 # -220 #
Micropowder: 240#-1200#
kinaiya
1. Ceramic surface treatment
2. F12-F2000
3. Grinding/Polishing
4. White Aluminium oxide
TECHNICAL DATA
paggamit |
paghingalan |
Kemikal nga% |
|||
Al2O3 |
Na2O |
Magnetic nga materyal% |
SiO2 |
||
abrasives |
H12 # -80 # |
≥99.4 |
≤0.4 |
- |
≤0.03 |
90 # -150 # |
≥99.3 |
≤0.4 |
≤0.03 |
≤0.05 |
|
180 # -240 # |
≥98.2 |
≤0.4 |
- |
≤0.03 |
|
1 # -63 # |
≥99.3 |
≤0.4 |
≤0.03 |
≤0.05 |
|
sa kalayo-resistant nga materyal |
180 # -0 200 # -0 320 # -0 |
≥99.3 |
≤0.4 |
≤0.06 |
≤0.05 |
micro powder |
0-1mm 1-3mm 3-5mm 5-8mm 8-12mm |
≥99 |
≤0.4 |
≤0.1 |
≤0.02 |
Kemikal nga komposisyon |
pisikal nga mga kabtangan |
|||
mga butang |
Bili sa paghingalan (%) |
mga butang |
Property |
|
Al2O3 |
99.18min |
kolor sa |
White |
|
SiO2 |
0.04max |
Bulk Densidad |
1.75-1.95g / cm3 |
|
Na2O |
0.40max |
sa matuod nga Densidad |
3.90g / cm3 min |
|
Fe2O3 |
0.08max |
katig-a |
Morse katig-a |
9 |
micro katig-a |
21600-22600kg / mm3 |
|||
sulod sa magnetic bahandi |
0,0023% max |
PAGGAMIT
Nagkasuod abrasives ug gibulitan abrasives
1.lapping, polishing,decorative non-skid tile, and pressure blasting.
2.Coated Abrasives
3.Surface treatment/finishing
4.Anti-Skid Paints
5.Ceramic Tiles special ceramics
6.Fluidized Bed Furnaces and Skin / Dental Care
7.grinding high carbon steel, high-speed steel and chilled steel