Reasonable price for Steel Shot-S280 to Frankfurt Factories
Short Description:
FEAUTRES Size: S280 Diameter: 0.8mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S280 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Reasonable price for Steel Shot-S280 to Frankfurt Factories Detail:
FEAUTRES
Size: S280
Diameter: 0.8mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S280
TECHNICAL DATA
Name |
Steel Shot |
|
Chemistry |
(C) |
0.70~1.20% |
(Mn) |
0.35~1.20% |
|
(Si) |
0.40~1.20% |
|
(S) |
≤0.05% |
|
(P) |
≤0.05% |
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
Deviation |
±3.0HRC(±40HV) |
|
Micro Structure |
Tempered martensite or tempered troostite |
|
Density |
7.2g/cm3 |
Product detail pictures:
Related Product Guide:
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
Garnet: The Ancient Stone Which Beholds Sheer Class
abide by the contract", conforms on the market requirement, joins within the market competition by its superior quality likewise as provides far more comprehensive and great company for shoppers to let them develop into huge winner. The pursue on the corporation, is definitely the clients' gratification for Reasonable price for Steel Shot-S280 to Frankfurt Factories, The product will supply to all over the world, such as: Belarus , Malaysia , Nairobi , The products has a good reputation with competitive price, unique creation, leading the industry trends. The company insists on the principle of win-win idea, has establishedglobal sales network and after-sales service network.
By Lesley from Doha - 2018.12.10 19:03
The product classification is very detailed that can be very accurate to meet our demand, a professional wholesaler.
By Heather from Finland - 2017.12.09 14:01