China wholesale Steel Shot-S660 to Slovak Republic Factory
Short Description:
FEAUTRES Size: S660 Diameter: 2.0mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S660 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
China wholesale Steel Shot-S660 to Slovak Republic Factory Detail:
FEAUTRES
Size: S660
Diameter: 2.0mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S660
TECHNICAL DATA
Name |
Steel Shot |
|
Chemistry |
(C) |
0.70~1.20% |
(Mn) |
0.35~1.20% |
|
(Si) |
0.40~1.20% |
|
(S) |
≤0.05% |
|
(P) |
≤0.05% |
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
Deviation |
±3.0HRC(±40HV) |
|
Micro Structure |
Tempered martensite or tempered troostite |
|
Density |
7.2g/cm3 |
Product detail pictures:
Related Product Guide:
Basic Information About Abrasive Garnet Processing
Garnet – Stone of Growth, Protection and Healing
Our merchandise are commonly identified and dependable by end users and will meet continually altering financial and social desires for China wholesale Steel Shot-S660 to Slovak Republic Factory, The product will supply to all over the world, such as: Senegal , Durban , Anguilla , If any item be of interest to you, you should let us know. We will try our best to satisfy your requirements with high quality goods, the best prices and prompt delivery. You should feel free to contact us at any time. We will reply you when we receive your inquiries. Make sure you note that samples are available before we start our business.
By Odelette from Malawi - 2018.09.21 11:01
The accounts manager made a detailed introduction about the product, so that we have a comprehensive understanding of the product, and ultimately we decided to cooperate.
By Nora from Lesotho - 2018.05.22 12:13