Factory making Steel Shot-S280 Wholesale to Mumbai
Short Description:
FEAUTRES Size: S280 Diameter: 0.8mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S280 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Factory making Steel Shot-S280 Wholesale to Mumbai Detail:
FEAUTRES
Size: S280
Diameter: 0.8mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S280
TECHNICAL DATA
Name |
Steel Shot |
|
Chemistry |
(C) |
0.70~1.20% |
(Mn) |
0.35~1.20% |
|
(Si) |
0.40~1.20% |
|
(S) |
≤0.05% |
|
(P) |
≤0.05% |
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
Deviation |
±3.0HRC(±40HV) |
|
Micro Structure |
Tempered martensite or tempered troostite |
|
Density |
7.2g/cm3 |
Product detail pictures:
Related Product Guide:
Basic Information About Abrasive Garnet Processing
Garnet: The Ancient Stone Which Beholds Sheer Class
It is a great way to further improve our products and repair. Our mission is always to create innovative products to prospects with a superior expertise for Factory making Steel Shot-S280 Wholesale to Mumbai, The product will supply to all over the world, such as: South Africa , Korea , Senegal , With the best technological support, we have tailored our website for the best user experience and kept in mind your ease of shopping. we ensure that the best reaches you at your doorstep, in the shortest possible time and with the help of our efficient logistical partners i.e DHL and UPS. We promise quality, living by the motto of promising only what we can deliver.
By Tina from Egypt - 2018.10.09 19:07
The manufacturer gave us a big discount under the premise of ensuring the quality of products, thank you very much, we will select this company again.
By Bess from Turkey - 2017.08.28 16:02