Chinese Professional Steel Shot-S170 to Congo Importers
Short Description:
FEATURES Size: S170 Diameter: 0.5mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S710 TECHNICAL DATA Name Steel shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Chinese Professional Steel Shot-S170 to Congo Importers Detail:
FEATURES
Size: S170
Diameter: 0.5mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S710
TECHNICAL DATA
Name |
Steel shot |
|
Chemistry |
(C) |
0.70~1.20% |
(Mn) |
0.35~1.20% |
|
(Si) |
0.40~1.20% |
|
(S) |
≤0.05% |
|
(P) |
≤0.05% |
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
Deviation |
±3.0HRC(±40HV) |
|
Micro Structure |
Tempered martensite or tempered troostite |
|
Density |
7.2g/cm3 |
Product detail pictures:
Related Product Guide:
Garnet: The Ancient Stone Which Beholds Sheer Class
Benefits of Garnet Abrasives
We know that we only thrive if we will guarantee our combined cost competiveness and high-quality advantageous at the same time for Chinese Professional Steel Shot-S170 to Congo Importers, The product will supply to all over the world, such as: Ireland , Korea , Florence , We follow superior mechanism to process these goods that ensure optimum durability and reliability of the goods. We follow latest effective washing and straightening processes that enable us to supply unmatched quality of items for our clients. We continually strive for perfection and all our efforts are directed towards attaining complete client satisfaction.
By Julie from Sri Lanka - 2017.11.11 11:41
This supplier's raw material quality is stable and reliable, has always been in accordance with the requirements of our company to provide the goods that quality meet our requirements.
By Poppy from Philippines - 2018.12.11 14:13